MP159 is a Nickel-Cobalt based multiphase alloy. This combination of properties enables ultra high strength, toughness, good ductility and excellent corrosion resistance. Through work strengthening and aging MP159 alloy exhibits ultimate tensile strength levels in excess of 1830 MPa.
MP159 is used in many different industries from use in prosthetic devices, jet engine components, fasteners, marine applications to petroleum industry applications.
|Density||8.33 g/cm³||0.301 lb/in³|
|Tensile strength (annealed 1052°C)||848 MPa||123000 psi|
|Yield strength (at strain 0.200%, annealed 1052°C)||400 MPa||58000 psi|
|Elastic modulus (at 232°C/450°F,annealed)||208 GPa||30200 ksi|
|Shear modulus (at 232°C/450°F,annealed)||75.8 GPa||11000 ksi|
|Elongation at break (cold worked 48%)||12%||12%|
|Reduction of area||46%||46%|
|Thermal expansion co-efficient (at 25-100°C/77-212°F)||14.3 µm/m°C||7.94 µin/in°F|
Bar, rod, sheet, wire
Landing gears and bolt material
Solid rocket boosters
Pulp and paper
Power generation equipment
Our MP 159 is carefully handled to minimize damage during storage and transportation and to preserve the quality of the product in its original condition.